9600H Electrophoresis Coating
Description:
| Lead Time | 10 - 15 days |
Quick Details
| High Corrosion Resistance | Smooth Coating | Uniform Coating | Even Deposition |
| Strong Adhesion | Enhanced Grip | Eco-Friendly | Environmentally Safe |
| Wide Industry Application | Versatile Use |
Product Details
Characteristic : 960H is a constituent of acrylic emulsion and paste. The main emulsion part is
acid neutralised reaction product of acrylic resin and cross linked with isocyanide and flexibilizer.
The colour paste incorporates epoxy dispersion, with dyes and filing materials through fine
grinding. Excellent electrodeposition abilities. Widely applied in electrodepostion for light industry
metal parts.
|
Item |
|
Specification |
|
Standard |
|
|
|
Emulsion |
Paste |
Reference |
|
Appearance |
|
Clear white fluid |
Paste(with dyes) |
Visual |
|
Volatility,weight% |
120℃,1h/2g,% |
38-42 |
43-44 |
HG/T3334.4.6 |
|
Fineness |
µm |
<10 |
<15 |
GB/T6753.1 |
|
pH Value |
25℃ |
6.0-7.3 |
- - |
HG/T3334.4.2 |
|
Conductivity |
25℃, µs/cm² |
1000-2000 |
- - |
HG/T3334.4.1 |
|
2. Bath Parameter |
|
|
|
|
|
Item |
|
Specifications |
|
Standard Reference |
|
Volatility,weight% |
120℃,1h/2g,% |
12-20 |
|
HG/T3334.4.6 |
|
pH Value |
25℃ |
5.6 - 6.6 |
|
HG/T3334.4.2 |
|
Conductivity |
25℃, µs/cm² |
800-1800 |
|
HG/T3334.4.1 |
|
Curing Time |
(26-30)℃, hour |
48 |
|
2L bath |
|
Bath Temperature |
℃ |
28 - 32 |
|
Thermometer |
|
Deposition Time |
S |
60 - 120 |
|
N/A |
|
Voltage |
V |
100 - 200 |
|
2L bath |
|
Curing Condition |
℃/min |
170-180 / 20 |
|
HG/T3334.4.17 |
|
Solvent Content |
% |
0.5 - 1.5 |
|
QB8008 |
|
MEQ Acid |
mmol/100g |
35 - 45 |
|
HG/T3334.4.13 |
|
Impact Voltage |
V |
≥250 |
|
HG/T3334.4.16 |
|
Dye-binder Ratio |
- - |
0.18 - 0.25 |
|
HG/T3334.4.8 |
|
Throwing Power |
%, (NV-20%) |
≥75 |
|
HG/T3334.4.3 5B |
|
|
|
|
Voltage/Time: |
280V/180S |